Silicone Rubber Material
Aug 28, 2017

Silicone Rubber Material Basic Info

  • Model NO.: MCSIL-S Silicone Rubber

  • Material: Silicone Rubber

  • Form: Liquid Rubber

  • Color: off-White

  • Mixed Viscosity: 12000-13000 Cps

  • Tear Strength: 20 N/Mm

  • Specification: REACH, MSDS, SGS

  • HS Code: 39100000

  • Raw Material: Silicone Rubber Raw Material

  • Appearance: Liquid

  • Item: Mcsil-S20

  • Mixing Ratio: 100:2

  • Hardness: 18-20 Shore a

  • Trademark: MC SILICONE

  • Origin: Dongguan, China

Silicone Rubber Material Product Description

Description of Shoe Sole Mold Making RTV2 Silicone Rubber

Shoe Sole Mold Making RTV2 Silicone Rubber is a two-component material, the silicone consists of Part A silicone base and Part B CA30 curing agent, and the silicone base and curing agent can cure at room temperature by a condensation reaction. These materials can be cast into the cured silicone mold: Shoe mold making, sand casting etc.

Silicone Rubber Material Specifications of Shoe Sole Mold Making RTV2 Silicone Rubber

1. Good flow ability and long working time
2. Medium hardness
3. Easy de-mould from shoe mold
4. Low linear shrinkage

Silicone Rubber Material Applications of Shoe Sole Mold Making RTV2 Silicone Rubber

MCSIL-S20 silicone rubber is suited for shoe mold, simple products, sand casting mold making, and shoe mold by pouring way.


How to make the silicone mold?

1. Preparing
The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.

2. Mixing
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100: 2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35C (95F). It's suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

3. Pouring the mixture and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

Storage of Shoe Sole Mold Making RTV2 Silicone Rubber

When the silicone rubber is stored at or below 30 C (85F) in the original unopened containers, RTV silicone base and CA30 curing agent have a usable life of 12 months from the date of production.

Note of Shoe Sole Mold Making RTV2 Silicone Rubber

RTV silicone rubber is an industrial product and must not be used in food molding, dental human skin molding applications.

Packing of Shoe Sole Mold Making RTV2 Silicone Rubber

Part A base silicone: 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 0.25kg/bottle, 1kg/bottle and 10kg/bottle

Need more information, please feel free to contact Nicole.

Item No.MCSIL-S20
Coloroff-white
Curing agentCA30
Mixing ratio100:2
Mixed viscosity12000-13000 cps
Hardness18-20 Shore A
Tear Strength20 N/mm